Glass

ABSTRACT

An alkali-free glass of the present invention includes as a glass composition, in terms of mass %, 55% to 70% of SiO2, 15% to 25% of Al2O3, 0% to 1% of B2O3, 0% to 0.5% of Li2O+Na2O+K2O, 2% to 6% of MgO, 2% to 8% of CaO, 0% to 4% of SrO, and 6% to 12% of BaO, and has a strain point of more than 720° C.

TECHNICAL FIELD

The present invention relates to a glass, and more specifically, to a glass suitable as a substrate for an OLED display.

BACKGROUND ART

An electronic device, such as an OLED display, is used in applications such as displays of cellular phones because the electronic device is thin, is excellent in displaying a moving image, and has low power consumption.

A glass sheet is widely used as a substrate for an OLED display. The glass sheet of this application is mainly required to satisfy the following characteristics.

(1) To have small contents of alkali metal oxides in order to prevent a situation in which alkali ions are diffused into a semiconductor substance having been formed into a film in a heat treatment step.

(2) To be excellent in productivity, particularly in devitrification resistance and meltability, in order to achieve a reduction in cost of the glass sheet.

(3) To have a high strain point in order to reduce thermal shrinkage in a production process for a p-Si TFT.

(4) To have a high specific Young's modulus in order to reduce deflection under its own weight in a conveyance step.

CITATION LIST Patent Literature

Patent Literature 1: JP 2009-525942 A

SUMMARY OF INVENTION Technical Problem

The above-mentioned item (3) is described in detail. The production process for a p-Si TFT includes a heat treatment step at from 400° C. to 600° C., and in the heat treatment step, the glass sheet causes a minute dimensional change called thermal shrinkage. When the thermal shrinkage is large, a TFT pixel pitch shift occurs, which results in a display defect. In the case of an OLED display, even a dimensional shrinkage of about several ppm may result in a display defect, and hence there is a demand for a glass sheet exhibiting less thermal shrinkage. As a heat treatment temperature of the glass sheet becomes higher, the thermal shrinkage is increased more.

As a method of reducing the thermal shrinkage of the glass sheet, there is given a method involving, after forming the glass sheet, performing annealing treatment at around an annealing point. However, the annealing treatment takes a long time period, and hence the production cost of the glass sheet is increased.

As another method, there is given a method involving increasing the strain point of the glass sheet. As the strain point becomes higher, the thermal shrinkage is less liable to occur in the production process for a p-Si TFT. For example, in Patent Literature 1, there is disclosed a glass sheet having a high strain point. However, when the strain point is high, productivity is liable to be reduced.

The present invention has been made in view of the above-mentioned circumstances, and a technical object of the present invention is to devise a glass which is excellent in productivity (particularly devitrification resistance) and has a high specific Young's modulus, and besides, exhibits less thermal shrinkage in a production process for a p-Si TFT.

Solution to Problem

The inventor of the present invention has repeatedly performed various experiments. As a result, the inventor has found that the technical object can be achieved by strictly restricting a glass composition and a strain point of low-alkali glass. Thus, the inventor proposes the finding as the present invention. That is, according to one embodiment of the present invention, there is provided a glass, comprising as a glass composition, in terms of mass %, 55% to 70% of SiO₂, 15% to 25% of Al₂O₃, 0% to 1% of B₂O₃, 0% to 0.5% of Li₂O+Na₂O+K₂O, 2% to 6% of MgO, 2% to 8% of CaO, 0% to 4% of SrO, and 6% to 12% of BaO, and having a strain point of more than 720° C. Herein, the content of “Li₂O+Na₂O+K₂O” refers to a total content of Li₂O, Na₂O, and K₂O. The “strain point” refers to a value measured in accordance with a method of ASTM C336.

Secondly, it is preferred that the glass according to the embodiment of the present invention have a ratio of SiO₂/Al₂O₃ in terms of mass % of 3.6 or less. Herein, the ratio of “SiO₂/Al₂O₃” in terms of mass % refers to a value obtained by dividing a content of SiO₂ by a content of Al₂O₃.

Thirdly, it is preferred that the glass according to the embodiment of the present invention comprise as a glass composition, in terms of mass %, 57% to 65% of SiO₂, 18% to 22% of Al₂O₃, 0% to less than 1% of B₂O₃, 0% to less than 0.1% of Li₂O+Na₂O+K₂O, 2% to 4% of MgO, 3% to 7% of CaO, 0% to 3% of SrO, and 7% to 11% of BaO.

Fourthly, it is preferred that the glass according to the embodiment of the present invention have a ratio of MgO/CaO in terms of mass % of from 0.5 to 0.9. Herein, the ratio of “MgO/CaO” in terms of mass % refers to a value obtained by dividing a content of MgO by a content of CaO.

Fifthly, it is preferred that the glass according to the embodiment of the present invention have a content of MgO+CaO+SrO+BaO (RO) of from 17.0 mass % to 19.1 mass %. Herein, the content of “MgO+CaO+SrO+BaO” refers to a total content of MgO, CaO, SrO, and BaO, that is, a total content of alkaline earth metal oxides.

Sixthly, it is preferred that the glass according to the embodiment of the present invention have a ratio of (MgO+CaO+SrO+BaO)/Al₂O₃ in terms of mass % of from 0.94 to 1.13. Herein, the ratio of “(MgO+CaO+SrO+BaO)/Al₂O₃” in terms of mass % refers to a value obtained by dividing a total content of MgO, CaO, SrO, and BaO by a content of Al₂O₃.

Seventhly, it is preferred that the glass according to the embodiment of the present invention have a ratio of SiO₂/Al₂O₃ in terms of mol % of from 5.4 to 5.9.

Eighthly, it is preferred that the glass according to the embodiment of the present invention further comprise 0.001 mass % to 1 mass % of SnO₂.

Ninthly, it is preferred that the glass according to the embodiment of the present invention have a specific Young's modulus, that is, a value obtained by dividing a Young's modulus by a density, of more than 29.5 GPa/g·cm³.

Tenthly, it is preferred that the glass according to the embodiment of the present invention have a temperature at a viscosity of 10^(2.5) dPa·s of 1,695° C. or less. Herein, the “temperature at a viscosity of 10^(2.5) dPa·s” may be measured by a platinum sphere pull up method.

Eleventhly, it is preferred that the glass according to the embodiment of the present invention have a liquidus temperature of less than 1,300° C. Herein, the “liquidus temperature” may be calculated by measuring a temperature at which a crystal precipitates when glass powder which has passed through a standard 30-mesh sieve (500 μm) and remained on a 50-mesh sieve (300 μm) is placed in a platinum boat and then kept for 24 hours in a gradient heating furnace.

Twelfthly, it is preferred that the glass according to the embodiment of the present invention have a viscosity at a liquidus temperature of 10^(4.8) dPa·s or more. Herein, the “viscosity at a liquidus temperature” may be measured by a platinum sphere pull up method.

Thirteenthly, it is preferred that the glass according to the embodiment of the present invention have a flat sheet shape and comprise overflow-joined surfaces in a middle portion thereof in a sheet thickness direction. That is, it is preferred that the glass according to the embodiment of the present invention be formed by an overflow down-draw method.

Fourteenthly, it is preferred that the glass according to the embodiment of the present invention be used for an OLED device.

DESCRIPTION OF EMBODIMENTS

A glass of the present invention comprises as a glass composition, in terms of mass %, 55% to 70% of SiO₂, 15% to 25% of Al₂O₃, 0% to 1% of B₂O₃, 0% to 0.5% of Li₂O+Na₂O+K₂O, 2% to 6% of MgO, 2% to 8% of CaO, 0% to 4% of SrO, and 6% to 12% of BaO. The reasons why the contents of the components are restricted as described above are hereinafter described. In the descriptions of the contents of the components, the expression “%” refers to “mass %” unless otherwise specified.

SiO₂ is a component which forms a glass skeleton and increases a strain point. The content of SiO₂ is from 55% to 70%, preferably from 58% to 65%, particularly preferably from 59% to 62%. When the content of SiO₂ is small, the strain point or acid resistance is liable to be reduced, and a density is liable to be increased. Meanwhile, when the content of SiO₂ is large, a viscosity at high temperature is increased, and thus meltability is liable to be reduced. Besides, a glass component balance is lost, and thus a devitrified crystal, such as cristobalite, precipitates, with the result that a liquidus temperature is liable to be increased. Further, an etching rate in HF is liable to be reduced.

Al₂O₃ is a component which increases the strain point. Further, Al₂O₃ is also a component which increases a Young's modulus. The content of Al₂O₃ is from 15% to 25%, preferably from 17% to 23%, from 18% to 22%, or from 18.2% to 21%, particularly preferably from 18.6% to 21%. When the content of Al₂O₃ is small, the strain point or a specific Young's modulus is liable to be reduced. Meanwhile, when the content of Al₂O₃ is large, mullite or a feldspar-based devitrified crystal precipitates, with the result that the liquidus temperature is liable to be increased.

The ratio of SiO₂/Al₂O₃ is an important component ratio for simultaneously achieving a high strain point, devitrification resistance, and meltability at a high level. These components each have an increasing effect on the strain point as described above, but when the amount of SiO₂ is relatively increased, a devitrified crystal, such as cristobalite, is liable to precipitate, and the meltability is liable to be reduced. Meanwhile, when the amount of Al₂O₃ is relatively increased, an alkaline earth aluminosilicate-based devitrified crystal, such as mullite or anorthite, is liable to precipitate. Therefore, the ratio of SiO₂/Al₂O₃ in terms of mass % is preferably from 2.5 to 4, from 2.6 to 3.6, or from 2.8 to 3.3, particularly preferably from 3.1 to 3.3. In addition, the ratio of SiO₂/Al₂O₃ in terms of mol % is preferably from 4.9 to 6.5 or from 5.2 to 6.0, particularly preferably from 5.4 to 5.9.

B₂O₃ is a component which increases the meltability and the devitrification resistance. The content of B₂O₃ is from 0% to 1%, preferably from 0.1% to less than 1% or from 0.3% to 0.75%, particularly preferably from 0.5% to 0.7%. When the content of B₂O₃ is small, the meltability is liable to be reduced, and the liquidus temperature is liable to be increased. Further, buffered hydrofluoric acid resistance (BHF resistance) is liable to be reduced. Meanwhile, when the content of B₂O₃ is large, the strain point, the acid resistance, and the specific Young's modulus are liable to be reduced. In addition, water is liable to be mixed in the glass from a raw material for introducing B₂O₃, and a β-OH value is liable to be increased. When the strain point is to be increased to the extent possible, the content of B₂O₃ is from 0% to less than 1% or from 0% to less than 0.1%, particularly preferably from 0% to less than 0.07%.

Li₂O, Na₂O, and K₂O are each a component which increases the meltability and reduces the electrical resistivity of molten glass. However, when Li₂O, Na₂O, and K₂O are incorporated in large amounts, there is a risk in that a semiconductor substance is contaminated owing to diffusion of alkali ions. Therefore, the content of Li₂O+Na₂O+K₂O is from 0% to 0.5%, preferably from 0.01% to 0.3% or from 0.02% to 0.2%, particularly preferably from 0.03% to less than 0.1%. In addition, the content of Na₂O is preferably from 0% to 0.3%, from 0.01% to 0.3%, or from 0.02% to 0.2%, particularly preferably from 0.03% to less than 0.1%.

MgO is a component which increases the meltability and the Young's modulus. The content of MgO is from 2% to 6%, preferably from 2% to 5% or from 2.5% to 4.5%, particularly preferably from 3% to 4%. When the content of MgO is small, it becomes difficult to ensure stiffness, and the meltability is liable to be reduced. Meanwhile, when the content of MgO is large, a devitrified crystal derived from mullite, Mg, or Ba and a devitrified crystal of cristobalite are liable to precipitate, and there is a risk in that the strain point is significantly reduced.

CaO is a component which reduces the viscosity at high temperature and thus remarkably increases the meltability without reducing the strain point. In addition, a raw material for introducing CaO is relatively inexpensive among those for alkaline earth metal oxides, and hence CaO is a component which achieves a reduction in raw material cost. Further, CaO is also a component which increases the Young's modulus. In addition, CaO also has a suppressing effect on the precipitation of the devitrified crystal containing Mg. The content of CaO is from 2% to 8%, preferably from 3% to 7% or from 3.5% to 6%, particularly preferably from 3.5% to 5.5%. When the content of CaO is small, it is difficult to exhibit the above-mentioned effects. Meanwhile, when the content of CaO is large, a devitrified crystal of anorthite is liable to precipitate and the density is liable to be increased.

The ratio of MgO/CaO in terms of mass % is an important component ratio for achieving both high devitrification resistance and a high specific Young's modulus. When the ratio of MgO/CaO in terms of mass % is small, the specific Young's modulus is liable to be reduced. Meanwhile, when the ratio of MgO/CaO in terms of mass % is large, the liquidus temperature is liable to be increased owing to a devitrified crystal containing Mg. Therefore, the ratio of MgO/CaO in terms of mass % is preferably from 0.4 to 1.5, from 0.5 to 1.0, or from 0.5 to 0.9, particularly preferably from 0.6 to 0.8.

SrO is a component which suppresses phase separation and increases the devitrification resistance. Further, SrO is also a component which reduces the viscosity at high temperature and thus increases the meltability without reducing the strain point. However, when the content of SrO is large, a feldspar-based devitrified crystal is liable to precipitate in such a glass system comprising CaO in a large amount as in the present invention, and the devitrification resistance is liable to be reduced contrarily. Further, there is a tendency that the density is increased or the Young's modulus is reduced. Therefore, the content of SrO is from 0% to 4%, preferably from 0% to 3%, from 0% to 2%, from 0% to 1.5%, or from 0% to 1%, particularly preferably from 0% to less than 1%. Meanwhile, when SrO is replaced with BaO, a reduction in Young's modulus can be suppressed, and further, an increase in density can also be suppressed. In order to obtain such effects, the content of SrO is preferably from 1% to 4% or from 2% to 4%, particularly preferably from 3% to 4%.

BaO is a component which has a high suppressing effect on the precipitation of a mullite-based or anorthite-based devitrified crystal, among alkaline earth metal oxides. The content of BaO is from 6% to 12%, preferably from 7% to 11% or from 8% to 10.7%, particularly preferably from 9% to 10.5%. When the content of BaO is small, the mullite-based or anorthite-based devitrified crystal is liable to precipitate. Meanwhile, when the content of BaO is large, the density is liable to be increased and the Young's modulus is liable to be reduced. In addition, the viscosity at high temperature is excessively increased, and thus the meltability is liable to be reduced.

The alkaline earth metal oxides are each a very important component for increasing the strain point, the devitrification resistance, and the meltability. When the content of the alkaline earth metal oxides is small, the strain point is increased. However, it becomes difficult to suppress the precipitation of an Al₂O₃-based devitrified crystal. In addition, the viscosity at high temperature is increased, and thus the meltability is liable to be reduced. Meanwhile, when the content of the alkaline earth metal oxides is large, the meltability is improved. However, the strain point is liable to be reduced. In addition, there is a risk in that the liquidus viscosity is reduced owing to a reduction in viscosity at high temperature. Therefore, the content of MgO+CaO+SrO+BaO is preferably from 16% to 20%, from 17% to 20%, or from 17.0% to 19.5%, particularly preferably from 18% to 19.3%.

The ratio of (MgO+CaO+SrO+BaO)/Al₂O₃ in terms of mass % is an important component ratio for reducing the liquidus viscosity through suppression of the precipitation of various devitrified crystals. When the ratio of (MgO+CaO+SrO+BaO)/Al₂O₃ in terms of mass % is small, the liquidus temperature of mullite is liable to be increased. Meanwhile, when the ratio of (MgO+CaO+SrO+BaO)/Al₂O₃ in terms of mass % is large, the alkaline earth metal oxides are increased, and a feldspar-based devitrified crystal or an alkaline earth metal-containing devitrified crystal is liable to precipitate. Therefore, the ratio of (MgO+CaO+SrO+BaO)/Al₂O₃ in terms of mass % is preferably from 0.80 to 1.20, from 0.84 to 1.15, or from 0.94 to 1.13, particularly preferably from 0.94 to 1.05.

Other than the above-mentioned components, for example, the following components may be added.

ZnO is a component which increases the meltability. However, when ZnO is incorporated in a large amount, the glass is liable to devitrify, and the strain point is liable to be reduced. Therefore, the content of ZnO is preferably from 0% to 5%, from 0% to 3%, or from 0% to 0.5%, particularly preferably from 0% to 0.2%.

P₂O₅ is a component which increases the strain point. However, when P₂O₅ is incorporated in a large amount, the glass is liable to undergo phase separation. Therefore, the content of P₂O₅ is preferably from 0% to 1.5% or from 0% to 1.2%, particularly preferably from 0% to less than 0.1%.

TiO₂ is a component which reduces the viscosity at high temperature and thus increases the meltability, and is also a component which suppresses solarization. However, when TiO₂ is incorporated in a large amount, the glass is colored, and thus a transmittance is liable to be reduced. Therefore, the content of TiO₂ is preferably from 0% to 5%, from 0% to 3%, from 0% to 1%, or from 0% to 0.1%, particularly preferably from 0% to 0.02%.

ZrO₂, Y₂O₃, Nb₂O₅, and La₂O₃ each have an action of increasing the strain point, the Young's modulus, and the like. However, when the contents of those components are large, the density is liable to be increased. Therefore, the content of each of ZrO₂, Y₂O₃, Nb₂O₅, and La₂O₃ is preferably from 0% to 5%, from 0% to 3%, from 0% to 1%, or from 0% to less than 0.1%, particularly preferably from 0% to less than 0.05%. Further, the total content of Y₂O₃ and La₂O₃ is preferably less than 0.1%.

SnO₂ is a component which exhibits a satisfactory fining action in a high temperature region. In addition, SnO₂ is a component which increases the strain point, and is also a component which reduces the viscosity at high temperature. The content of SnO₂ is preferably from 0% to 1%, from 0.001% to 1%, or from 0.01% to 0.5%, particularly preferably from 0.05% to 0.3%. When the content of SnO₂ is large, a devitrified crystal of SnO₂ is liable to precipitate. When the content of SnO₂ is small, it becomes difficult to exhibit the above-mentioned effects.

F₂, Cl₂, SO₃, C, or metal powder, such as Al powder or Si powder, may be added at up to 5% as a fining agent as long as glass characteristics are not impaired. In addition, CeO₂ or the like may also be added at up to 1% as a fining agent.

As₂O₃ and Sb₂O₃ each act effectively as a fining agent. However, from an environmental viewpoint, it is preferred to use those components as little as possible, while the glass of the present invention does not completely exclude the introduction of those components. Further, when As₂O₃ is incorporated in a large amount in the glass, the solarization resistance tends to be reduced. Therefore, the content of As₂O₃ is preferably 0.1% or less, and the glass is desirably substantially free of As₂O₃. Herein, the “substantially free of As₂O₃” refers to a case in which the content of As₂O₃ in the glass composition is less than 0.05%. In addition, the content of Sb₂O₃ is preferably 0.2% or less, particularly preferably 0.1% or less, and the glass is desirably substantially free of Sb₂O₃. Herein, the “substantially free of Sb₂O₃” refers to a case in which the content of Sb₂O₃ in the glass composition is less than 0.05%.

Fe₂O₃ is a component which reduces the electrical resistivity of the molten glass. The content of Fe₂O₃ is preferably from 0.001% to 0.1% or from 0.005% to 0.05%, particularly preferably from 0.008% to 0.015%. When the content of Fe₂O₃ is small, it becomes difficult to exhibit the above-mentioned effect. Meanwhile, when the content of Fe₂O₃ is large, a transmittance in an ultraviolet region is liable to be reduced, and at the time of using a laser in an ultraviolet region in a step of a display, irradiation efficiency is liable to be reduced. When electric melting is performed, it is preferred to positively introduce Fe₂O₃. In this case, the content of Fe₂O₃ is preferably from 0.005% to 0.03% or from 0.008% to 0.025%, particularly preferably from 0.01% to 0.02%. In addition, in order to increase the transmittance in an ultraviolet region, the content of Fe₂O₃ is preferably 0.020% or less, 0.015% or less, or 0.011% or less, particularly preferably 0.010% or less.

Cl has a promoting effect on the melting of low-alkali glass. When Cl is added, a melting temperature can be reduced, and the action of the fining agent can be promoted. In addition, Cl has a reducing effect on the β-OH value of the molten glass. However, when the content of Cl is too large, the strain point is liable to be reduced. Therefore, the content of Cl is preferably 0.5% or less, particularly preferably from 0.001% to 0.2%. As a raw material for introducing Cl, a raw material such as a chloride of an alkaline earth metal, such as strontium chloride, or aluminum chloride may be used.

The glass of the present invention preferably has the following glass characteristics.

In the glass of the present invention, the strain point is more than 720° C., preferably 730° C. or more or 740° C. or more, particularly preferably from 750° C. to 850° C. When the strain point is low, a glass sheet is liable to cause thermal shrinkage in a production process for a p-Si TFT.

The density is preferably 2.68 g/cm³ or less, 2.66 g/cm³ or less, or 2.65 g/cm³ or less, particularly preferably 2.64 g/cm³ or less. When the density is large, the specific Young's modulus is decreased, and the glass is liable to be deflected under its own weight.

The average thermal expansion coefficient within a temperature range of from 30° C. to 380° C. is preferably from 34×10⁻⁷/° C. to 43×10⁻⁷/° C., particularly preferably from 38×10⁻⁷/° C. to 41×10⁻⁷/° C. When the average thermal expansion coefficient within a temperature range of from 30° C. to 380° C. is outside the above-mentioned range, the average thermal expansion coefficient does not match the thermal expansion coefficient of a peripheral member, and peeling of the peripheral member or warpage of the glass sheet is liable to occur. Herein, the “average thermal expansion coefficient within a temperature range of from 30° C. to 380° C.” refers to a value measured with a dilatometer.

The etching rate in HF is preferably 0.8 μm/min or more or 0.9 μm/min or more, particularly preferably 1 μm/min or more. When the etching rate in HF is low, it becomes difficult to reduce the thickness of the glass sheet in a slimming step. Herein, the “etching rate in HF” refers to a value calculated from an etching depth when, after part of a surface of a mirror-polished glass is masked with a polyimide tape, the glass is etched under the conditions of 30 minutes in a 5 mass % HF aqueous solution at 20° C.

The liquidus temperature is preferably less than 1,300° C., 1,280° C. or less, or 1,260° C. or less, particularly preferably 1,240° C. or less. When the liquidus temperature is high, a devitrified crystal is generated during forming by an overflow down-draw method or the like, and the productivity of the glass sheet is liable to be reduced.

The viscosity at a liquidus temperature is preferably 10^(4.2) dPa·s or more, 10^(4.4) dPa·s or more, 10^(4.6) dPa·s or more, or 10^(4.8) dPa·s or more, particularly preferably 10^(5.0) dPa·s or more. When the viscosity at a liquidus temperature is low, a devitrified crystal is generated during forming by an overflow down-draw method or the like, and the productivity of the glass sheet is liable to be reduced.

The temperature at a viscosity of 10^(2.5) dPa·s is preferably 1,695° C. or less, 1,660° C. or less, 1,640° C. or less, or 1,630° C. or less, particularly preferably from 1,500° C. to 1,620° C. When the temperature at a viscosity of 10^(2.5) dPa·s is high, it becomes difficult to melt the glass, and the production cost of the glass sheet is increased.

The specific Young's modulus is preferably more than 29.5 GPa/g·cm⁻³, 30 GPa/g·cm⁻³ or more, 30.5 GPa/g·cm⁻³ or more, 31 GPa/g·cm⁻³ or more, or 31.5 GPa/g·cm⁻³ or more, particularly preferably 32 GPa/g·cm⁻³ or more. When the specific Young's modulus is low, the glass sheet is liable to be deflected under its own weight.

A method of reducing the β-OH value is exemplified by the following methods: (1) a method involving selecting raw materials having low water contents; (2) a method involving adding a component (such as Cl or SO₃) which reduces the water content in the glass; (3) a method involving reducing the water content in a furnace atmosphere; (4) a method involving performing N₂ bubbling in the molten glass; (5) a method involving adopting a small melting furnace; (6) a method involving increasing the flow rate of the molten glass; and (7) a method involving adopting an electric melting method.

Herein, the “β-OH value” refers to a value determined by using the following equation after measuring the transmittances of the glass with an FT-IR. β-OH value=(1/X)log(T ₁ /T ₂)

X: Glass thickness (mm)

T₁: Transmittance (%) at a reference wavelength of 3,846 cm⁻¹

T₂: Minimum transmittance (%) at a wavelength around a hydroxyl group absorption wavelength of 3,600 cm⁻¹

It is preferred that the glass of the present invention have a flat sheet shape and comprise overflow-joined surfaces in a middle portion thereof in a sheet thickness direction. That is, it is preferred that the glass of the present invention be formed by an overflow down-draw method. The overflow down-draw method refers to a method in which molten glass is caused to overflow from both sides of a wedge-shaped refractory, and the overflowing molten glasses are subjected to down-draw downward at the lower end of the wedge-shaped refractory while being joined, to thereby form a glass in a flat sheet shape. By the overflow down-draw method, surfaces which are to serve as the surfaces of a glass sheet are formed in a state of free surfaces without being brought into contact with the refractory. As a result, a glass sheet having good surface quality can be produced without polishing at low cost, and an increase in area and a reduction in thickness are easily achieved as well.

Other than the overflow down-draw method, the glass sheet may also be formed by, for example, a slot down method, a redraw method, a float method, or a roll-out method.

In the glass of the present invention, the thickness (in the case of having a flat sheet shape, a sheet thickness) is not particularly limited, but is preferably 1.0 mm or less, 0.7 mm or less, or 0.5 mm or less, particularly preferably 0.4 mm or less. As the sheet thickness becomes smaller, the weight of an OLED device can be reduced more easily. The thickness may be adjusted by controlling, for example, a flow rate and a sheet-drawing speed at the time of glass production.

As a method of industrially producing the glass of the present invention, there is preferably given a method of producing a glass sheet comprising as a glass composition, in terms of mass %, 55% to 70% of SiO₂, 15% to 25% of Al₂O₃, 0% to 1% of B₂O₃, 0% to 0.5% of Li₂O+Na₂O+K₂O, 2% to 6% of MgO, 2% to 8% of CaO, 0% to 4% of SrO, and 6% to 12% of BaO, and having a strain point of more than 720° C., the method comprising: a melting step of loading a blended glass batch into a melting furnace and heating the blended glass batch through application of a current with a heating electrode to provide molten glass; and a forming step of forming the resultant molten glass into a glass in a flat sheet shape having a sheet thickness of from 0.1 mm to 0.7 mm by an overflow down-draw method.

In general, a production process for the glass sheet comprises a melting step, a fining step, a supplying step, a stirring step, and a forming step. The melting step is a step of melting a glass batch obtained by blending glass raw materials to provide molten glass. The fining step is a step of fining the molten glass obtained in the melting step by an action of a fining agent or the like. The supplying step is a step of transferring the molten glass from one step to another. The stirring step is a step of stirring the molten glass to homogenize the molten glass. The forming step is a step of forming the molten glass into a glass in a flat sheet shape. A step other than the above-mentioned steps, for example, a state adjusting step of adjusting the molten glass to be in a state suitable for forming may be introduced after the stirring step as required.

When the conventional low-alkali glass is industrially produced, the melting has been generally performed by heating with combustion burner flame. A burner is generally arranged at an upper portion of a melting kiln, and uses fossil fuel as its fuel, specifically, for example, liquid fuel, such as heavy oil, or gas fuel, such as LPG. The combustion flame may be obtained by mixing the fossil fuel and oxygen gas. However, such method is liable to entail an increase in β-OH value because a large amount of water is mixed in the molten glass during the melting. Therefore, in the production of the glass of the present invention, it is preferred to perform heating through application of a current with a heating electrode, and it is preferred to perform the melting by heating through application of a current with a heating electrode without heating with combustion burner flame. With this, water is less liable to be mixed in the molten glass during the melting, and hence the β-OH value is easily controlled to 0.30/mm or less, 0.25/mm or less, 0.20/mm or less, or 0.15/mm or less, particularly 0.10/mm or less. Further, when the heating through application of a current with a heating electrode is performed, the amount of energy required for obtaining the molten glass per unit mass is reduced, and the amount of a melt volatile is reduced. As a result, an environmental load can be reduced.

The heating through application of a current with a heating electrode is preferably performed by applying an alternating voltage to a heating electrode arranged at a bottom portion or a side portion of a melting kiln so as to be brought into contact with the molten glass in the melting kiln. A material used for the heating electrode preferably has heat resistance and corrosion resistance to the molten glass. For example, tin oxide, molybdenum, platinum, or rhodium may be used, and molybdenum is particularly preferred from the viewpoint of a degree of freedom of arrangement in a furnace.

The glass of the present invention has a small content of an alkali metal oxide, and hence has a high electrical resistivity. Therefore, when the heating through application of a current with a heating electrode is applied to the low-alkali glass, there is a risk in that the current flows not only in the molten glass but also in a refractory constituting the melting kiln, with the result that the refractory constituting the melting kiln is damaged early. In order to prevent such situation, it is preferred to use, as a refractory in a furnace, a zirconia-based refractory having a high electrical resistivity, particularly zirconia electrocast bricks. In addition, it is preferred to introduce a component which reduces the electrical resistivity (Li₂O, Na₂O, K₂O, Fe₂O₃, or the like) in the molten glass (glass composition) in a small amount. In particular, it is preferred to introduce Li₂O, Na₂O, K₂O, or the like in a small amount. In addition, the content of Fe₂O₃ is preferably from 0.005 mass % to 0.03 mass % or from 0.008 mass % to 0.025 mass %, particularly preferably from 0.01 mass % to 0.02 mass %. Further, the content of ZrO₂ in the zirconia-based refractory is preferably 85 mass % or more, particularly preferably 90 mass % or more.

EXAMPLES

The present invention is hereinafter described by way of Examples.

Examples of the present invention (Sample Nos. 1 to 50) are shown in Tables 1 to 3. In the tables, the “N. A.” means that the item is not measured.

TABLE 1 No. 1 No. 2 No. 3 No. 4 No. 5 No. 6 No. 7 No. 8 No. 9 No. 10 Composition (mass %) SiO₂ 61.58 61.58 60.89 60.18 60.34 59.65 61.31 60.92 61.20 61.13 Al₂O₃ 19.39 19.39 19.45 19.50 20.75 20.80 19.09 19.08 19.17 19.14 B₂O₃ 0.30 0.30 0.30 0.30 0.30 0.30 0.30 0.30 0.30 0.29 Li₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.01 K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 MgO 3.57 3.57 4.17 4.77 3.55 4.14 3.69 3.80 4.11 3.81 CaO 3.09 3.09 3.10 3.11 3.07 3.08 3.17 3.25 3.27 3.67 SrO 3.16 3.16 3.17 3.18 3.14 3.15 3.31 3.31 2.57 2.56 BaO 8.68 8.68 8.71 8.73 8.63 8.65 8.90 9.12 9.16 9.15 ZnO 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 SnO₂ 0.22 0.22 0.22 0.22 0.22 0.22 0.22 0.22 0.22 0.22 Fe₂O₃ 0.008 0.009 0.011 0.013 0.015 0.016 0.017 0.012 0.012 0.012 mass SiO₂/Al₂O₃ 3.18 3.18 3.13 3.09 2.91 2.87 3.21 3.19 3.19 3.19 mol SiO₂/Al₂O₃ 5.39 5.39 5.31 5.24 4.94 4.87 5.45 5.42 5.42 5.42 MgO/CaO 1.15 1.15 1.34 1.53 1.15 1.34 1.16 1.17 1.26 1.04 RO 18.50 18.50 19.14 19.79 18.39 19.03 19.07 19.48 19.11 19.20 RO/Al₂O₃ 0.95 0.95 0.98 1.01 0.89 0.91 1.00 1.02 1.00 1.00 Property α 30-380 38.5 38.5 39.1 39.6 37.9 38.8 39.2 39.9 39.3 39.7 (×10⁻⁷/° C.) Density (g/cm³) 2.644 2.645 2.655 2.667 2.653 2.664 2.654 2.661 2.653 2.653 β-OH (mm⁻¹) 0.12 N.A. N.A. N.A. N.A. N.A. N.A. N.A. N.A. N.A. HF etching rate N.A. N.A. N.A. N.A. N.A. N.A. N.A. N.A. N.A. N.A. (μm/min.) Ps (° C.) 761 761 755 750 765 759 756 753 754 754 Ta (° C.) 819 820 812 807 822 816 814 812 812 812 Ts (° C.) 1.054 1.053 1.043 1.033 1.052 1.042 1.048 1.043 1.043 1.043 10^(4.5) dPa · s (° C.) 1.315 1.312 1.296 1.278 1.304 1.288 1.305 1.299 1.298 1.297 10^(4.0) dPa · s (° C.) 1.377 1.374 1.356 1.337 1.364 1.347 1.367 1.361 1.359 1.358 10^(3.0) dPa · s (° C.) 1.540 1.537 1.515 1.492 1.522 1.503 1.529 1.524 1.519 1.518 10^(2.5) dPa · s (° C.) 1.643 1.643 1.617 1.590 1.623 1.602 1.633 1.629 1.622 1.620 TL (° C.) 1.231 1.246 1.268 1.279 1.272 1.277 1.269 1.261 1.270 1.263 Logη at TL 5.28 5.11 4.75 4.50 4.79 4.60 4.83 4.85 4.75 4.81 (dPa · s) Young's modulus 83.9 84.1 84.6 85.4 84.9 85.6 84.1 84.1 84.4 84.1 (GPa) Specific modulus 31.7 31.8 31.9 32.0 32.0 32.1 31.7 31.6 31.8 31.7 (GPa/g · cm⁻³) No. 11 No. 12 No. 13 No. 14 No. 15 No. 16 No. 17 No. 18 No. 19 No. 20 Composition (mass %) SiO₂ 61.05 60.52 61.38 60.85 61.02 60.46 61.35 61.12 61.56 61.63 Al₂O₃ 19.36 19.33 19.11 19.08 19.79 20.19 19.51 19.44 19.58 19.60 B₂O₃ 0.29 0.29 0.00 0.00 0.50 0.70 1.02 1.01 1.02 1.02 Li₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.01 0.01 0.01 0.00 0.00 0.00 0.00 0.00 0.00 0.00 K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 MgO 3.56 3.56 3.74 3.74 3.56 3.55 3.59 3.58 3.60 3.90 CaO 3.09 3.08 3.10 3.09 3.09 3.08 3.52 3.51 3.95 3.54 SrO 3.15 3.15 3.16 3.16 3.15 3.15 3.18 2.41 2.43 2.43 BaO 8.67 8.65 8.69 8.68 8.66 8.64 7.61 8.70 7.64 7.65 ZnO 0.59 1.18 0.59 1.18 0.00 0.00 0.00 0.00 0.00 0.00 SnO₂ 0.22 0.22 0.22 0.22 0.22 0.22 0.22 0.22 0.22 0.22 Fe₂O₃ 0.012 0.012 0.020 0.012 0.011 0.011 0.010 0.015 0.009 0.012 mass SiO₂/Al₂O₃ 3.15 3.13 3.21 3.19 3.08 2.99 3.14 3.14 3.14 3.14 mol SiO₂/Al₂O₃ 5.35 5.31 5.45 5.41 5.23 5.08 5.34 5.34 5.34 5.34 MgO/CaO 1.15 1.15 1.21 1.21 1.15 1.15 1.02 1.02 0.91 1.10 RO 18.47 18.45 18.70 18.67 18.46 18.43 17.91 18.20 17.62 17.52 RO/Al₂O₃ 0.95 0.95 0.98 0.98 0.93 0.91 0.92 0.94 0.90 0.89 Property α 30-380 39.0 38.9 39.2 39.2 38.4 38.5 38.1 38.3 38.0 37.6 (×10⁻⁷/° C.) Density (g/cm³) 2.657 2.668 2.659 2.672 2.644 2.648 2.624 2.632 2.617 2.616 β-OH (mm⁻¹) N.A. N.A. N.A. N.A. N.A. N.A. N.A. 0.10 N.A. N.A. HF etching rate N.A. N.A. N.A. N.A. N.A. N.A. N.A. N.A. N.A. N.A. (μm/min.) Ps (° C.) 754 750 757 752 758 756 750 750 750 750 Ta (° C.) 813 807 814 809 816 814 808 809 808 808 Ts (° C.) 1.045 1.038 1.046 1.039 1.049 1.046 1.041 1.042 1.040 1.040 10^(4.5) dPa · s (° C.) 1.302 1.293 1.304 1.295 1.307 1.302 1.297 1.299 1.298 1.294 10^(4.0) dPa · s (° C.) 1.364 1.354 1.366 1.356 1.368 1.363 1.358 1.361 1.360 1.355 10^(3.0) dPa · s (° C.) 1.525 1.512 1.525 1.513 1.528 1.520 1.517 1.523 1.522 1.513 10^(2.5) dPa · s (° C.) 1.629 1.613 1.627 1.616 1.630 1.619 1.622 1.628 1.626 1.614 TL (° C.) 1.265 1.264 1.264 1.264 1.271 1.255 1.239 1.240 1.240 1.260 Logη at TL 4.84 4.77 4.87 4.78 4.82 4.94 5.04 5.05 5.04 4.82 (dPa · s) Young's modulus 84.2 84.6 84.6 84.9 84.1 84.4 83.6 83.3 83.8 83.9 (GPa) Specific modulus 31.7 31.7 31.8 31.8 31.8 31.9 31.9 31.7 32.0 32.1 (GPa/g · cm⁻³)

TABLE 2 No. 21 No. 22 No. 23 No. 24 No. 25 No. 26 No. 27 No. 28 No. 29 No. 30 Composition (mass %) SiO₂ 61.56 61.62 61.76 61.91 62.01 61.42 61.52 61.42 61.73 61.74 Al₂O₃ 19.05 19.07 19.11 19.16 19.19 19.14 19.04 19.00 19.10 19.10 B₂O₃ 0.51 0.00 0.00 0.00 0.00 0.51 0.71 0.41 1.02 0.71 Li₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.02 Na₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 MgO 3.59 3.59 3.31 3.02 2.73 3.01 3.47 3.35 3.30 3.34 CaO 3.93 4.34 5.17 6.01 6.84 6.00 3.76 3.76 4.51 4.60 SrO 2.42 2.42 1.67 0.91 0.00 0.91 1.96 1.96 1.36 1.52 BaO 8.73 8.74 8.76 8.78 9.02 8.77 8.72 8.71 8.75 8.75 ZnO 0.00 0.00 0.00 0.00 0.00 0.00 0.59 1.19 0.00 0.00 SnO₂ 0.22 0.22 0.22 0.22 0.22 0.22 0.22 0.22 0.22 0.22 Fe₂O₃ 0.012 0.012 0.012 0.011 0.011 0.012 0.007 0.014 0.012 0.012 mass SiO₂/Al₂O₃ 3.23 3.23 3.23 3.23 3.23 3.21 3.23 3.23 3.23 3.23 mol SiO₂/Al₂O₃ 5.48 5.48 5.48 5.48 5.48 5.45 5.48 5.48 5.48 5.48 MgO/CaO 0.91 0.83 0.64 0.50 0.40 0.50 0.92 0.89 0.73 0.73 RO 18.66 19.09 18.90 18.71 18.58 18.70 17.92 17.77 17.93 18.23 RO/Al₂O₃ 0.98 1.00 0.99 0.98 0.97 0.98 0.94 0.94 0.94 0.95 Property α 30-380 39.1 39.5 39.9 40.2 40.4 40.1 38.0 38.2 N.A. 39.2 (×10⁻⁷/° C.) Density (g/cm³) 2.640 2.649 2.643 2.636 2.632 2.634 2.637 2.649 N.A. 2.627 β-OH (mm⁻¹) N.A. 0.11 N.A. N.A. N.A. N.A. N.A. N.A. N.A. 0.09 HF etching rate N.A. N.A. N.A. N.A. N.A. N.A. N.A. N.A. N.A. 0.97 (μm/min.) Ps (° C.) 753 758 758 758 759 749 748 746 745 750 Ta (° C.) 810 816 815 815 816 806 806 804 804 808 Ts (° C.) 1.043 1.045 1.045 1.044 1.045 1.036 1.040 1.040 1.039 1.041 10^(4.5) dPa · s (° C.) 1.301 1.303 1.301 1.300 1.301 1.293 1.301 1.295 1.297 1.296 10^(4.0) dPa · s (° C.) 1.363 1.365 1.362 1.361 1.362 1.355 1.363 1.356 1.358 1.357 10^(3.0) dPa · s (° C.) 1.526 1.526 1.522 1.521 1.523 1.515 1.525 1.516 1.518 1.519 10^(2.5) dPa · s (° C.) 1.630 1.629 1.625 1.623 1.625 1.618 1.628 1.618 1.621 1.622 TL (° C.) 1.249 1.246 1.249 1.269 1.281 1.249 1.249 1.247 N.A. 1.232 Logη at TL 4.98 5.02 4.98 4.78 4.67 4.90 4.97 4.95 N.A. 5.10 (dPa · s) Young's modulus 84.0 84.5 84.6 84.4 84.2 84.0 84.0 84.4 N.A. 83.4 (GPa) Specific modulus 31.8 31.9 32.0 32.0 32.0 31.9 31.9 31.9 N.A. 31.7 (GPa/g · cm⁻³) No. 31 No. 32 No. 33 No. 34 No. 35 No. 36 No. 37 No. 38 No. 39 No. 40 Composition (mass %) SiO₂ 61.41 61.91 61.78 61.76 61.67 61.10 63.90 61.50 61.60 63.60 Al₂O₃ 19.00 19.16 19.12 19.05 19.02 18.60 16.60 18.80 18.30 17.00 B₂O₃ 0.71 0.72 0.61 0.71 0.71 0.67 0.30 0.70 0.70 0.30 Li₂O 0.02 0.02 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.02 0.02 0.02 0.02 K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 MgO 3.09 3.35 3.48 3.12 3.11 3.20 1.87 3.10 3.44 1.73 CaO 4.90 4.69 4.35 4.91 4.90 5.11 5.98 5.17 3.64 5.98 SrO 0.60 1.83 2.12 0.61 0.30 0.62 0.81 0.61 3.15 0.77 BaO 10.05 8.10 8.31 9.62 10.06 10.40 10.50 9.96 9.03 10.40 ZnO 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 SnO₂ 0.22 0.22 0.22 0.22 0.22 0.22 0.18 0.21 0.21 0.21 Fe₂O₃ 0.010 0.012 0.016 0.012 0.015 0.014 0.010 0.009 0.012 0.011 mass SiO₂/Al₂O₃ 3.23 3.23 3.23 3.24 3.24 3.28 3.85 3.27 3.37 3.74 mol SiO₂/Al₂O₃ 5.48 5.48 5.48 5.50 5.50 5.59 6.53 5.55 5.71 6.35 MgO/CaO 0.63 0.72 0.80 0.63 0.63 0.63 0.31 0.60 0.95 0.29 RO 18.66 17.99 18.27 18.26 18.38 19.33 19.16 18.84 19.26 18.88 RO/Al₂O₃ 0.98 0.94 0.96 0.96 0.97 1.04 1.15 1.00 1.05 1.11 Property α 30-380 39.6 39.1 38.8 39.0 39.1 39.4 N.A. 39.5 39.3 N.A. (×10⁻⁷/° C.) Density (g/cm³) 2.638 2.621 2.628 2.629 2.631 2.638 N.A. 2.629 2.639 N.A. β-OH (mm⁻¹) 0.04 0.08 N.A. 0.15 0.07 0.05 N.A. N.A. N.A. 0.11 HF etching rate 1.00 0.97 N.A. N.A. N.A. 1.17 N.A. N.A. N.A. N.A. (μm/min.) Ps (° C.) 750 750 750 750 751 751 753 749 748 754 Ta (° C.) 809 808 808 809 809 809 814 807 805 815 Ts (° C.) 1.042 1.041 1.042 1.043 1.044 1.042 1.059 1.043 1.044 1.062 10^(4.5) dPa · s (° C.) 1.299 1.296 1.298 1.300 1.301 1.301 1.328 1.302 1.305 1.339 10^(4.0) dPa · s (° C.) 1.360 1.357 1.359 1.362 1.362 1.362 1.393 1.364 1.367 1.405 10^(3.0) dPa · s (° C.) 1.521 1.520 1.518 1.524 1.524 1.526 1.566 1.525 1.530 1.578 10^(2.5) dPa · s (° C.) 1.623 1.625 1.620 1.628 1.628 1.633 1.675 1.627 1.633 1.693 TL (° C.) 1.220 1.236 1.243 1.220 1.230 1.218 N.A. 1.231 1.223 N.A. Logη at TL 5.25 5.06 5.01 5.26 5.16 5.27 N.A. 5.17 5.27 N.A. (dPa · s) Young's modulus 83.4 83.6 84.0 83.1 83.0 83.1 N.A. 83.1 83.0 N.A. (GPa) Specific modulus 31.6 31.9 31.9 31.6 31.5 31.5 N.A. 31.6 31.5 N.A. (GPa/g · cm⁻³)

TABLE 3 No. 41 No. 42 No. 43 No. 44 No. 45 No. 46 No. 47 No. 48 No. 49 No. 50 Composition (mass %) SiO₂ 61.50 61.60 61.30 61.10 61.10 61.10 61.10 60.80 60.10 60.20 Al₂O₃ 18.50 18.20 18.40 18.50 18.60 18.70 18.50 18.30 18.60 17.30 B₂O₃ 0.70 0.70 0.80 0.90 0.80 0.80 0.80 0.70 0.90 0.80 Li₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.02 0.02 0.02 0.03 0.03 0.02 0.02 0.02 0.02 0.02 K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 MgO 3.09 3.09 3.44 3.44 3.08 3.02 3.38 3.42 2.95 1.80 CaO 5.18 5.17 3.65 3.64 5.15 5.15 3.80 3.62 5.22 6.24 SrO 0.62 0.61 3.17 3.16 0.77 0.46 3.17 3.30 0.46 1.50 BaO 10.20 10.40 9.01 9.01 10.40 10.60 9.01 9.66 11.50 11.90 ZnO 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 SnO₂ 0.21 0.21 0.21 0.21 0.21 0.20 0.20 0.20 0.21 0.20 Fe₂O₃ 0.011 0.011 0.010 0.008 0.012 0.013 0.010 0.010 0.009 0.014 mass SiO₂/Al₂O₃ 3.32 3.38 3.33 3.30 3.28 3.27 3.30 3.32 3.23 3.48 mol SiO₂/Al₂O₃ 5.64 5.74 5.65 5.60 5.57 5.54 5.60 5.64 5.48 5.91 MgO/CaO 0.60 0.60 0.94 0.95 0.60 0.59 0.89 0.94 0.57 0.29 RO 19.09 19.27 19.27 19.25 19.40 19.23 19.36 20.00 20.13 21.44 RO/Al₂O₃ 1.03 1.06 1.05 1.04 1.04 1.03 1.05 1.09 1.08 1.24 Property α 30-380 (×10⁻⁷/° C.) 39.1 39.9 39.2 39.4 39.5 39.2 39.3 40.0 40.5 42.8 Density (g/cm³) 2.632 2.635 2.640 2.640 2.640 2.639 2.642 2.656 2.655 2.675 β-OH (mm⁻¹) 0.14 0.14 0.14 0.14 0.12 0.11 0.12 0.12 0.10 0.10 HF etching rate N.A. N.A. N.A. N.A. N.A. N.A. N.A. N.A. N.A. N.A. (μm/min.) Ps (° C.) 744 744 744 744 746 748 745 745 743 738 Ta (° C.) 804 803 803 803 804 806 804 803 802 796 Ts (° C.) 1.042 1.041 1.041 1.040 1.040 1.042 1.041 1.040 1.035 1.032 10^(4.5) dPa · s (° C.) 1.301 1.303 1.303 1.300 1.299 1.299 1.300 1.301 1.294 1.296 10^(4.0) dPa · s (° C.) 1.363 1.365 1.365 1.362 1.361 1.361 1.362 1.363 1.356 1.360 10^(3.0) dPa · s (° C.) 1.527 1.528 1.528 1.524 1.524 1.524 1.524 1.526 1.518 1.527 10^(2.5) dPa · s (° C.) 1.632 1.633 1.633 1.629 1.627 1.627 1.628 1.631 1.618 1.632 TL (° C.) 1.222 1.220 1.219 1.223 1.231 1.232 1.227 1.231 1.228 1.233 Logη at TL (dPa · s) 5.24 5.27 5.29 5.22 5.21 5.13 5.18 5.14 5.11 5.07 Young's modulus (GPa) 83.1 82.9 83.3 83.3 83.2 83.1 83.2 83.0 82.5 81.2 Specific modulus 31.6 31.5 31.5 31.6 31.5 31.5 31.5 31.3 31.1 30.4 (GPa/g· cm⁻³)

First, a glass batch prepared by blending glass raw materials so that each glass composition listed in the tables was attained, placed in a platinum crucible, and then melted at from 1,600° C. to 1,650° C. for 24 hours. When the glass batch was dissolved, molten glass was stirred to be homogenized by using a platinum stirrer. Next, the molten glass was poured on a carbon sheet and formed into a sheet shape, followed by being annealed at a temperature around an annealing point for 30 minutes. Each of the resultant samples was evaluated for its average thermal expansion coefficient α within a temperature range of from 30° C. to 380° C., density (Density), β-OH value, etching rate in HF (HF etching rate), strain point Ps, annealing point Ta, softening point Ts, temperature at a viscosity of 10^(4.5) dPa·s, temperature at a viscosity of 10^(4.0) dPa·s, temperature at a viscosity of 10^(3.0) dPa·s, temperature at a viscosity of 10^(2.5) dPa·s, liquidus temperature TL and liquidus viscosity log η at TL, Young's modulus (Young's modulus), and specific Young's modulus (Specific modulus).

The average thermal expansion coefficient α within a temperature range of from 30° C. to 380° C. is a value measured with a dilatometer.

The density is a value measured by a well-known Archimedes method.

The β-OH value is a value measured by the above-mentioned method.

The etching rate in HF is a value calculated from an etching depth when, after part of a surface of the resultant glass, which has been mirror polished, is masked with a polyimide tape, the glass is etched under the conditions of 30 minutes in a 10 mass % HF aqueous solution at 20° C.

The strain point Ps, the annealing point Ta, and the softening point Ts are values measured in accordance with methods of ASTM C336 and C338.

The temperatures at viscosities at high temperature of 10^(4.5) dPa·s, 10^(4.0) dPa·s, 10^(3.0) dPa·s, and 10^(2.5) dPa·s are values measured by a platinum sphere pull up method.

The liquidus temperature TL is a value obtained by measuring a temperature at which a crystal (initial phase) precipitates when glass powder which has passed through a standard 30-mesh sieve (sieve opening: 500 μm) and remained on a 50-mesh sieve (sieve opening: 300 μm) is placed in a platinum boat and kept for 24 hours in a gradient heating furnace.

The liquidus viscosity log₁₀ηTL is a value obtained by measuring the viscosity of a glass at the liquidus temperature TL by a platinum sphere pull up method.

The Young's modulus is a value measured by a well-known resonance method. The specific Young's modulus is a value obtained by dividing the Young's modulus by the density.

As apparent from Tables 1 to 3, each of Sample Nos. 1 to 50 had small contents of alkali metal oxides, and had a strain point of 738° C. or more, a temperature at a viscosity of 10^(2.5) dPa·s of 1,693° C. or less, a liquidus temperature of 1,281° C. or less, a viscosity at a liquidus temperature of 10^(4.50) dPa·s or more, and a specific Young's modulus of 30.4 GPa/g·cm⁻³ or more. Therefore, it is considered that each of Sample Nos. 1 to 50 can be suitably used as a substrate for an OLED display. 

The invention claimed is:
 1. A glass, comprising as a glass composition, in terms of mass %, 55% to 61.60% of SiO₂, 15% to 25% of Al₂O₃, 0% to 1% of B₂O₃, 0% to 0.5% of Li₂O+Na₂O+K₂O, 2% to 6% of MgO, 2% to 8% of CaO, 0% to 4% of SrO, and 6% to 12% of BaO, and having a strain point of more than 720° C., wherein the glass has a ratio of SiO₂/Al₂O₃ in terms of mass % of 3.6 or less, and wherein the glass has a temperature at a viscosity of 10^(2.5) dPa·s of 1,695° C. or less.
 2. The glass according to claim 1, wherein the glass composition comprises, in terms of mass %, 57% to 61.60% of SiO₂, 18% to 22% of Al₂O₃, 0% to less than 1% of B₂O₃, 0% to less than 0.1% of Li₂O+Na₂O+K₂O, 2% to 4% of MgO, 3% to 7% of CaO, 0% to 3% of SrO, and 7% to 11% of BaO.
 3. The glass according to claim 1, wherein the glass has a ratio of MgO/CaO in terms of mass % of from 0.5 to 0.9.
 4. The glass according to claim 1, wherein the glass has a content of MgO+CaO+SrO+BaO of from 17.0 mass % to 19.1 mass %.
 5. The glass according to claim 1, wherein the glass has a ratio of (MgO+CaO+SrO+BaO)/Al₂O₃ in terms of mass % of from 0.94 to 1.13.
 6. The glass according to claim 1, wherein the glass has a ratio of SiO₂/Al₂O₃ in terms of mol % of from 5.4 to 5.9.
 7. The glass according to claim 1, further comprising 0.001 mass % to 1 mass % of SnO₂.
 8. The glass according to claim 1, wherein the glass has a specific Young's modulus of more than 29.5 GPa/g·cm⁻³.
 9. The glass according to claim 1, wherein the glass has a liquidus temperature of less than 1,300° C.
 10. The glass according to claim 1, wherein the glass has a viscosity at a liquidus temperature of 10^(4.8) dPa·s or more.
 11. The glass according to claim 1, wherein the glass has a flat sheet shape and comprises overflow-joined surfaces in a middle portion thereof in a sheet thickness direction.
 12. An organic light-emitting diode (OLED) device comprising the glass according to claim
 1. 